PA6-CF Material

PA6-CF is a composite material in which carbon fibers are embedded within a polyamide 6 matrix. This combination results in a material with improved mechanical properties compared to standard PA6, including higher tensile strength, stiffness, and resistance to deformation. PA6-CF is commonly used in applications requiring high-performance materials, such as automotive components, aerospace parts, sporting goods, and industrial machinery components. Its lightweight and strong characteristics make it suitable for applications where weight reduction and structural integrity are critical.

characteristics of PA6-CF.

  1. High Strength: PA6-CF exhibits high tensile strength and stiffness due to the reinforcement of carbon fibers. This makes it suitable for applications requiring structural integrity and load-bearing capabilities.
  2. Lightweight: Despite its high strength, PA6-CF remains lightweight due to the low density of carbon fibers. This property contributes to weight reduction in components and structures, particularly in aerospace and automotive applications where minimizing mass is critical.
  3. Dimensional Stability: PA6-CF shows excellent dimensional stability and resistance to deformation, even under mechanical stress and varying environmental conditions. This property ensures the integrity and precision of parts and components over time.
  4. Abrasion Resistance: The presence of carbon fibers enhances the abrasion resistance of PA6-CF, making it highly resistant to wear and friction. This property extends the lifespan of components subjected to repetitive movement and contact.
  5. Heat Resistance: PA6-CF exhibits good heat resistance, allowing it to maintain its mechanical properties at elevated temperatures. This property makes it suitable for applications exposed to high temperatures, such as engine components and industrial machinery.

Overall, PA6-CF is a high-performance composite material known for its combination of strength, lightweight, dimensional stability, abrasion resistance, and heat resistance. It finds applications in various industries, including automotive, aerospace, sporting goods, and industrial manufacturing, where demanding performance requirements are essential. Its versatility and superior properties make it a preferred choice for applications where lightweight, strong, and durable materials are necessary.

Material Properties

PA6-CF (Nylon 6)

Physical Properties

  • Density - 1.09 g/cm³
  • Vicat Softening Temp - 212 °C
  • Heat Deflection Temp - 186 °C
  • Melting Temp - 223 °C
  • Melt Index - 6.8 ± 0.6 g/10 min

Mechanical Properties

  • Tensile Strength - 102 ± 7 MPa
  • Breaking Elongation Rate - 5.8 ± 1.6%
  • Bending Modulus - 5460 ± 280 MPa
  • Bending Strength - 151 ± 8 MPa
  • Impact Strength - 40.3 ± 2.5 kJ/m²